Increase the service life of the mill roll and reduce the production cost


Description:The article focuses on the analysis of the hot-rolled narrow strip in the middle of the rolling groove, such as irregular deblocking, cracking of the roll ring, pitting of the roll groove, etc. Effectively improve the cooling effect of the roller table, and appropriately increase the width of the roller ring to avoid cracks and falling off, and select the appropriate roller material.

Keyword:Steel mill roll life

By optimizing the steel rolling process and improving the performance of the roll device and other technical measures, the hardness, thermal crack resistance and impact resistance of the roll have been effectively improved and greatly improved, and the service life of the roll has been extended while reducing the consumption of the roll.

The article focuses on the analysis of the hot-rolled narrow strip in the middle of the rolling groove, such as irregular deblocking, cracking of the roll ring, pitting of the roll groove, etc. Effectively improve the cooling effect of the roller table, and appropriately increase the width of the roller ring to avoid cracks and falling off, and select the appropriate roller material.

Steel mill roll life

The importance of extending roll life

The roll is an important work piece that undergoes continuous plastic deformation of the metal in a rolling mill and is highly consumable. It accounts for a large portion of production costs. Through the perfect roll management system, managers can clearly know the condition and track of each roll, make the correct pairing and use of the rolls, maximize the utilization rate of the rolls, and formulate the appropriate grinding amount, which can not only reduce the fatigue of the rolls, Make the rolls meet the standard for normal production of the machine, increase the life of the rolls, reduce abnormal roll changes, improve the production efficiency of the rolling line, and increase production benefits. Whether the roll management system is sound or not, and the degree of management, etc., are the key factors to reduce the production cost of the rolling line and prolong the service life of the roll.

Special personnel are required to manage the rolls, establish a roll management system, and make records of rolls entering the warehouse for acceptance, matching use, roll cracks, and abnormal off-machines. Through a series of such operations, the use trajectory of each roll and the state of the rolls will be managed and controlled, which is crucial for reducing roll consumption and increasing roll service life.

Problems with rolls in production

Irregular drop in the center of the rolling groove

There are too many chemical components containing copper in the central parts of the rolling groove, which will easily lead to irregular block falling. Especially whenever the central part of the entire rolling groove is heated, a large amount of copper may flow back and forth continuously on the inner wall surface of the central part of the entire rolling groove. Once the copper forms a low temperature melting point, it will directly make its thermoplastic performance greatly improved. Reduced, which in turn will lead to many cracks on the surface of the inner layer. Moreover, as the copper flows back and forth, the cracks will continue to expand and extend, and to a certain extent, the problem of irregular falling blocks will appear. Taking hot-rolled narrow strip steel as an example, due to the lack of daily supervision, the rolling volume of each groove is controlled by the finished product adjuster, so the wear of each groove is inconsistent. When the roll is repaired, the cracks in individual grooves are not completely turned. Due to the existence of microscopic cracks, when it is used again on the line, the microcracks grow rapidly and connect, and finally lead to the generation of macroscopic cracks, resulting in the loss of meat in the rolling groove.

Roll ring cracking

Roll rings and rolls are affected by assembly stress, thermal stress and rolling stress during the rolling process. The stress on the roller ring is the algebraic sum of the stress values along the section. In the rolling process, the tangential tensile stress of the inner diameter of the roll ring is large, and the use of a single material roll ring is not conducive to improving the service life of the roll. At the same time, due to the increase in the local stress of the roller ring, coupled with the effects of other stresses, the roller ring is also easily damaged, causing it to crack.

Pitting in the rolling groove

Pitting on the rolling groove is a common surface defect. Its appearance is rough and uneven, also known as “pitting”. Most are continuous, but a few are partial or sporadic. Pitting This defect is allowed in the groove, but its depth cannot exceed the thickness deviation of the product. Causes of pimples are:

(1) The finished hole or front hole is worn, or there is damaged iron oxide.

(2) After being extruded to the surface of the rolled piece, the broken iron oxide is peeled off.

(3) The roll is corroded.

(4) During heating, the surface of the billet is severely oxidized.

Roll breakage

During the rolling process, cracks and soft spots are formed on the surface and inside of the roll due to impact, tail flicking, steel clamping and other reasons. The cracks and soft spots of the roll will seriously affect the normal production of the rolling line and the service life of the roll. Severe cracks can cause premature spalling of the roll, ending the roll’s life prematurely.

The reasons for these problems are: improper human operation, poor cooling effect, key points of rolling material production technology, quality problems of the roll itself, etc. Improper or inappropriate cooling will generate a large temperature difference on the surface of the roller, thereby accelerating the thermal stress of the roller falling off. At the same time, if the temperature of the roller is too high, it will also affect the strength and wear resistance of the roller, resulting in burst grooves, Problems such as debonding, burning and even breaking. In production, if the characteristics of the rolled material and the production process are not considered, the selected roll material is not suitable, or due to human factors such as rolling rolls, stacking steel, etc., there will also be problems such as bursting, meat loss, and roll breakage. .

In actual production operations, since metallurgical steel materials often contain brittle inclusions such as SiO2, Al2O3 or silicate, the existence of these inclusions can easily have a serious impact on the service life of the roll, and according to the number, size, Different types have different effects on the life of the roll. In general, the more inclusions and the larger their size, the more harmful they are.

Process measures

Improvement of roll cooling device

In order to improve the utilization efficiency of cooling water and enhance the cooling effect of cooling water, the method of improving the performance of the roll cooling device can be adopted to prolong the service life of the roll. The rolling mill will generate a lot of heat during the rolling process. Therefore, cooling is required to ensure the replacement cycle, service life and temperature after processing of the rolls. Two cooling water tanks for the roll, primary cooling water and secondary cooling water, the primary cooling water is sprayed axially to the rolling area through the slit to lubricate and cool the copper tube; the secondary cooling is to quickly reduce the temperature of the rolled tube , to avoid air flow into the rolling envelope, to prevent oxidation of copper tubes. The water spray ring of the cooling device of the roll is used to cool the roll.

During rolling, the main transmission speed is above 1300rpm, and the auxiliary transmission (roller) is above 700rpm. The rolls work at such a high speed that the flow and pressure of the cooling water need to be strictly controlled. The cooling water must be continuously and sufficiently cooled. If the roll temperature is too high, it must be replaced in time to prevent thermal fatigue cracking. In actual production, in order to ensure that the temperature of the roll is not too high and maintain temperature stability, it is necessary to ensure that the cooling rate of the roll is above 3500L/h, and the pressure of the water pump should be below 0.8MPa.

From the original square box-type structure with holes to the solid cylindrical nozzle, two rows of elliptical water seams are added to the split wedge, and the width of the split wedge covered by the water seams is 5~8mm; to ensure the safety of the split wedge The water is 3 times that of other parts to enhance the cooling degree of the cutting wedge and improve the groove life of the cutting wedge.

Optimization of cooling water parameters and improvement of water supply system

Choose the appropriate cooling water temperature, if it is too high, it will accelerate the fracture of the roll, if it is lowered, it will affect the recrystallization of the rolled tube and the quality of the product, if it is extremely low temperature and extreme high temperature, it will accelerate fatigue, so, in During production, the cooling water temperature of the roll should be 40~60°C.

The roll cooling water pipeline has been improved, from low turbid water supply to medium turbid water supply, and the water pump motor adopts frequency conversion motor to make the water pressure reach 0.8MPa, and the water pressure can be automatically adjusted.

Optimization of pass configuration

Due to the unsatisfactory effect of cooling water, on the basis of the original pass of the hot-rolled narrow strip steel φ550, the pass of the I-stand rolling mill adopts the principle of forced widening. In view of the high temperature of K1 steel, the pass of forced widening is set at For K3 and K4, the bottom of the forced widening groove is designed as a straight line. At the same time, in order to avoid wrinkles on the surface of the rolled piece and cause unqualified surface quality of the finished product, the slope of the forced widening pass is set at 17.7°, and the K3 1. After K4 adopts forced widening, corresponding changes are made to K6’s rolling groove size to ensure that there will be no tailing phenomenon.

Roll material optimization

Taking Q215 hot-rolled narrow-strip commonly used varieties as an example, the center distance between the initial rolling grooves is 19.0mm, and the width of the middle roll ring is 7.8mm, which has reached the theoretical design index. However, from the point of view of the overall fracture of the roll ring, the width of the roll ring is still very narrow, which is prone to cracks under fatigue conditions, and finally causes the roll ring to crack. For this reason, from the perspective of roll length, a roll gap of 22.0 mm is designed, and the width of the middle roll ring is adjusted to 10.8 mm.

Automatic control thickness configuration modification

Due to the influence of the entrance thickness, tension, friction coefficient, deformation resistance and other factors, the rolling force of the rolling mill will also change accordingly, and the related deformation curve will have a certain impact on the thickness of the exit. Automatic thickness control (Automatic Controller Controller, AGC) mainly uses model algorithms to automatically control strip thickness, rolling equipment conditions, external disturbances, etc., so as to automatically set the juicing pressure, speed, and the size of the roll gap of the rolling mill, and ensure reasonable thickness deviation. Usually AGC adopts a hydraulic press-down system, which has high precision and correspondingly is relatively fast. The quality control of the rolling mill has a certain relationship with the precise control of the thickness of the slab, and the number of hydraulic QGC equipment will have a certain impact on the precision of the rolling mill. Steel wire finish rolling No. 6 rolling mill, the rough rolling control thickness is (27~2.7) mm, and the deviation rate is 10%.

Avoid improper operation

In the production process, roll damage caused by improper use is also very common. Therefore, it is necessary to prevent direct contact between the guide and the roll. Second, the cooling water switch of the roll must be strictly implemented to prevent the replaced head from being dehydrated. Third, spot checks must be strengthened to prevent problems with the rolls. Once rolls appear, the machine must be stopped immediately, and the processing can only be stopped after the winding roll material cools down to room temperature. Fourth, the material shape of the rolled piece must be strictly controlled in accordance with the process system to prevent the phenomenon that the material shape of a single rack is too large. Fifth, the blackhead on the head of the rolled piece should be cut clean, and black steel is prohibited.

The amount of repair should be in place 

In order to ensure that the output of each rolling groove can maintain a relatively stable state, no redundant cracks can appear, otherwise, the rolling capacity of the rolling mill will be greatly reduced, and if there are redundant cracks, it will affect the quality of the product. have a great impact. Therefore, during the rolling process, the rolling must be carried out strictly according to the regulations. For example, the turning amount of the finished roll of Q215 hot-rolled narrow strip steel must reach 600mm.

By taking the above measures, the service life of the rolls can be greatly increased, the number of roll replacements can be reduced, and the labor intensity of workers can be reduced. By correcting the uneven drop in the middle of the roll, the problems of roll ring cracks and pitting are solved, and the grooves caused by cooling are almost zero, thereby improving the quality of the product. Increase in average effective productivity.

Generally it is 5-10 days if the goods are in stock. or it is 15-20 days if the goods are not in stock, it is according to quantity.

A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 30% T/T in advance ,balance before shippment.

Always a pre-production sample before mass production;
Always final Inspection before shipment;
During the epidemic, provide remote detection technical support

Tell us a little about your application and we’ll get back to you to finalize a quotation to meet your needs as quickly as possible.

Rolling mill rolls product

Classification by roll material:

Cast iron mill rolls

  • Alloy indefinite chilled cast iron rolls
  • Alloy chilled cast iron rolls
  • Alloy SG ductile cast iron roll
  • Pearlitic ductile cast iron roll
  • Bainite ductile cast iron roll
  • Centrifugal cast iron roll

Cast steel mill rolls   

  • Alloy cast steel rolls
  • Semi-steel roller
  • Graphite steel rolls
  • High-chromium steel roll
  • High-speed steel roll

Forging mill rolls

Sort by position on the rolling mill:

Work rolls
backup rolls

Intermediate roll

Product advantage

The world No. 1 in crude steel production steel plant, over 70% of the HSS for bar and wire are from us.

LMM high-speed steel rolls have higher steel passing per groove (times) due to their good wear resistance, which saves roll changing time, improves rolling mill operation rate, reduces roll consumption, and improve the overall efficiency of the factory.
Generally, the amount of steel passing in a single groove (times) is 3 to 5 times that of cast iron rolls.