Cemented carbide roll rings, composed of tungsten carbide and binding metal, is one kind of tool material with high hardness and good wear-resistance. In order to make full use of the above advantages of cemented carbide roll rings, the manufacturer of high-speed wire rod shall pay more attention to the following items duringthe course of purchasing and using it

1. Make the correct choice for the cemented carbide used by the fnishing mill

Before determining the grade of cemented carbide for every stand, we shall have a thorough understand about their properties so as to make the correct choice (Please refer to the preceding paragraph)

2. Installation of cemented carbide roll rings

The sleeve insertion and assmbly of cemented carbide roll rings shall be carried out in accordance with
the requirements of precision. There shall be appropriate space between the roll rings and axle or
between the roll rings and sleeve. The fit is neither tight nor loose. You should check whether the roll rings
conforms to the technological requirement and clean the mounting surface of roll rings, sleeve and axle
before the installation. It is prohibited to beat the roll rings with hammer or other hard things while
assemblying.

3. Requirement for the cooling of roll rings and cooling water during the course of rolling

Because of the negative effect of heat corrosion, thermal fatigue and thermal stress, the net-shaped thermal fatigue crack usually appears while the collar working. With the increase of cracks, small parts may come off and even the roll rings is broken. We adopt the cooling method to reduce the bad effect prevent the cracks from stretching and prolong the durability of rolling groove, which plays an positive role on the cemented carbide roll rings The parameters of cooling water are as follows: temperature no more than 35C, pressure of o. 4-0. 6 Mpa volume of 24-30 m3 per stand per hour, radical direction for spraying water, the angle of 15-30between the spraying direction and rotating direction of roll rings. The water is twice as wide as the rolling groove and directly sprayed into the groove without scattering

Cooling water quality requirement 

1. For ygh series medium or weak alkali water of ph> 7 2 

2. For ygr series or phs7. 2 weak water< 15 milligram/L acid water of ph> 7. 2 

3. The content of solid particles in the

tungsten carbide ring rolls

4. Determine the reasonal yield

It is inevitable to find the microcrack on the rolling groove. The microcrack will gradually extend, stretch and
deepen. The groove shall be repaired immediately while the depth of crack reaching 0.2-0.4 mm. Otherwise,
the crack will deepen quickly, which leads to a risk of broken roller. The range of normal yield is regulated
as follows:
Stands of pre-finishing rolling mill : (5000-7000) tons
1-2 Stands of finishing rolling mill: (2000-3000) tons
3-4 Stands of finishing rolling mill: (2000-3000) tons
5-6 Stands of finishing rolling mill: (1500 -2500) tons
7-8 Stands of finishing ralling mill: (1500- 2500) tons
9-10 Stands of finishing rolling mill: (1200-2000) tons
Stands for reducing diameters: (1000-1 500) tons

4. Determine the reasonal yield

It is inevitable to find the microcrack on the rolling groove. The microcrack will gradually extend, stretch and
deepen. The groove shall be repaired immediately while the depth of crack reaching 0.2-0.4 mm. Otherwise,
the crack will deepen quickly, which leads to a risk of broken roller. The range of normal yield is regulated
as follows:
Stands of pre-finishing rolling mill : (5000-7000) tons
1-2 Stands of finishing rolling mill: (2000-3000) tons
3-4 Stands of finishing rolling mill: (2000-3000) tons
5-6 Stands of finishing rolling mill: (1500 -2500) tons
7-8 Stands of finishing ralling mill: (1500- 2500) tons
9-10 Stands of finishing rolling mill: (1200-2000) tons
Stands for reducing diameters: (1000-1 500) tons

5. Repair of groove

It is normal to find the microcrack on the rolling groove. The groove shall be repaired immediately while the
depth of crack reaching 0.2 mm. It is necessary to prevent the roller from being broken. While repairing, we
must ensure to remove the crack thoroughly. Otherwise, it will bring a potential risk to next rolling. It is
difficult and inconvenient to check if the surface is polishing. To ensure the complete remove of microcrack,
we can increase the grinding quantity.
Under the normal condition, the repair is controlled in the range of:
1. Roll rings for stands 9-10 of finishing rolling mill: (0.4-0.6) mm
2. Roll rings for stands 1-8 of finishing roiling mill: (0.7-1.2) mm
3. Roll rings for stands of pre-finishing rolling mill: (1 .2-2.0) mm

Generally it is 5-10 days if the goods are in stock. or it is 15-20 days if the goods are not in stock, it is according to quantity.

A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 30% T/T in advance ,balance before shippment.

Always a pre-production sample before mass production;
Always final Inspection before shipment;
During the epidemic, provide remote detection technical support

Tell us a little about your application and we’ll get back to you to finalize a quotation to meet your needs as quickly as possible.

Rolling mill rolls product

Classification by roll material:

Cast iron mill rolls

  • Alloy indefinite chilled cast iron rolls
  • Alloy chilled cast iron rolls
  • Alloy SG ductile cast iron roll
  • Pearlitic ductile cast iron roll
  • Bainite ductile cast iron roll
  • Centrifugal cast iron roll


Cast steel mill rolls   

  • Alloy cast steel rolls
  • Semi-steel roller
  • Graphite steel rolls
  • High-chromium steel roll
  • High-speed steel roll


Forging mill rolls

Sort by position on the rolling mill:

Work rolls
backup rolls

Intermediate roll

Product advantage

The world No. 1 in crude steel production steel plant, over 70% of the HSS for bar and wire are from us.

LMM high-speed steel rolls have higher steel passing per groove (times) due to their good wear resistance, which saves roll changing time, improves rolling mill operation rate, reduces roll consumption, and improve the overall efficiency of the factory.
Generally, the amount of steel passing in a single groove (times) is 3 to 5 times that of cast iron rolls.